Adhesive tape

ABSTRACT

An adhesive tape is provided which comprises a film of high density polyethylene having a density of not less than 0.94 g/cc elongated at least six times only transversely to the longitudinal direction of the tape and a layer of pressure sensitive adhesive applied at least on one side of said elongated film of high density polyethylene. The adhesive tape has a high tensile strength against a force applied in a direction transverse to the longitudinal direction of the tape. Nevertheless, the tape can be easily torn or cut by user&#39;s hand or hands exactly transversely to the longitudinal direction of the tape without being torn zigzag or in a slanting direction.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to an adhesive tape, and more particularly to an adhesive tape which may be conveniently used as a sealing tape for containers made of, for example corrugated cardboard or as a splicing adhesive tape for butt joining seams of elongated paper, cloth, film or the like.

2. Prior Art

Hithertofore there has been known an adhesive tape of the type for use as a splicing adhesive tape comprising a film of cellophane paper, kraft paper, polypropylene or the like as a substrate and a pressure sensitive adhesive applied to one side or both sides of the film. The adhesive tape of this type, however, has a disadvantage that it has less strength against a force applied in a lateral or transverse direction so that it can often readily be torn or cut off, particularly when it has a slight rent on its edge. To avoid such disadvantage there has been used a film of polyesters as a substrate which has relatively high strength. However, polyester films are quite expensive. Therefore, the tape of such type has not been widely used.

Alternatively, an adhesive tape for sealing, for example corrugated cardboard containers has been known in which paper, fabrics, a polypropylene film or a polyvinyl chloride film is used as a substrate, a pressure sensitive adhesive being applied to one side or both sides of the substrate. The adhesive sealing tape of the type in which paper is used as a substrate is not strong enough to seal containers filled with relatively heavy contents. Accordingly, a reinforced paper backed with various plastic films or fablics has been used as a substrate material. However, the reinforced paper adhesive tape has drawbacks that it is quite difficult to cut by hand or hands and even if it can, the tape has a tendency to cut zigzag or in a slanting direction. Therefore, one has to utilize a special cutting device, which results in inefficient packing operation. In addition, when a reinforcing plastic film or fabric is adhered to the substrate paper, it is generally required to use a special adhesive or primer due to weak affinity between the reinforcing material and the substrate paper. Consequently, complicate steps for applying adhesives and for receiving solvents are necessarily involved for the production of such reinforced paper adhesive tape. In the meanwhile, the adhesive sealing tape of the type in which a polypropylene film or a polyvinyl film is used as a substrate, has inferior properties at low temperature such as brittleness. Furthermore, polyethylene or polyvinylchloride has large stiffness as shown by bending test as well as large coefficient of tensile elasticity at an elongation of 5%. Hence, when the tape comprising a film of these materials is used for sealing packages containing cold contents such as frozen food or used under low temperatures, the bent portions of the tape tends to stretch so that the tape gets turned or tucks up and peels off out of the packages.

OBJECTS AND SUMMARY OF THE INVENTION

It is an object of the present invention to provide an adhesive tape which can be easily cut by user's hand or hands exactly in a transverse direction to the longitudinal direction of the tape and which nevertheless has a high tensile strength against a force applied in the same direction.

It is another object of the present invention to provide an adhesive tape which is cheap and therefore can be widely used.

It is still another object of the invention to provide an adhesive tape which can be produced in a simple manner.

It is a still further object of the invention to provide an adhesive tape which has excellent coldproof properties.

These and other objects of the invention will become apparent with reference to the following description.

An adhesive tape according to the invention comprises a film of high density polyethylene having a density of not less than 0.94 g/cc elongated at least six times only in a transverse direction to the longitudinal direction of the tape and a layer of pressure sensitive adhesive applied at least one side of said elongated film of high density polyethylene. A second layer of pressure sensitive adhesive may be applied to the other side of said film of high density polyethylene. A base paper material may also be sandwiched between the film of high density polyethylene and the pressure sensitive adhesive.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view showing an adhesive tape of rolled type according to the invention.

FIG. 2 is a schematic sectional view taken along line 2--2 of FIG. 1.

FIG. 3 is a schematic sectional view similar to FIG. 2 but showing another form of an adhesive tape according to the present invention.

DESCRIPTION OF THE INVENTION

Referring to FIG. 1, an adhesive tape of rolled type is generally indicated by reference numeral 10. It is, however, to be understood that the adhesive tape according to the invention is not limited only to the rolled type. In FIG. 2, an adhesive tape consisting of a film 20 of high density polyethylene and a layer 21 of pressure sensitive adhesive applied to one side of the film is shown. Although not shown in the accompanying drawings, a second layer of pressure sensitive adhesive may be applied to the other side of the film 20. In FIG. 3, another embodiment of the present invention is illustrated in which a paper adhesive tape 30 consists of a film 20 of high density polyethylene, a base paper material 31, a layer 32 of low density polyethylene sandwiched between the film 20 and the paper material 31 and a layer 21 of pressure sensitive adhesive applied to the paper material 31.

In any forms of the adhesive tape it is of great importance that a film of high density polyethylene having a density of not less than 0.94 g/cc elongated at least six times, preferably ten times only transversely to the longitudinal direction of the tape be used. In this connection, it is to be noted that "transversely or a transverse direction" herein referred to means a direction a shown by an arrow in FIG. 1, whereas "longitudinally or a longitudinal direction" herein referred to means a direction b denoted by an arrow in FIG. 1 which crosses at a right angle with the arrow a. The reason why a high density polyethylene film of not less than 0.94 g/cc is used according to the invention is that a high strength against a transversely applied force is provided and that this characteristic does not disappear even at low temperatures. That is, the adhesive tape of high density polyethylene of not less than 0.94 g/cc has a stiffness of 8 to 16 g and a coefficient of tensile elasticity at an elongation of 5% of less than 90 kg/mm². Therefore, such tape will not become brittle nor hardened under cold atmosphere so as to be intimately and yet firmly adhered to surfaces to be applied even to bent portions such as corners of a container. When a polyethylene film having a density of less than 0.94 g/cc is used, the advantages above mentioned cannot be obtained.

Furthermore, when the aforementioned high density polyethylene film is elongated only transversely not less than six times, the elongated film has an improved tensile strength against a force applied in a transverse direction and at the same time a lowered tear strength against a force applied in the same direction. Accordingly, the adhesive tape comprising such polyethylene film can be easily torn or cut by user's hand or hands exactly transversely without using cutters. Nevertheless, the tape retains a high tensile strength so that even when a transverse stress acts on the tape, it will not break or peel off. If the high density polyethylene film is elongated not less than ten times, the characteristic properties as set forth can be further enhanced. However, it is not possible to produce an effective elongated film at an elongation above sixteen times.

An adhesive tape having a density of less than 0.94 g/cc and/or elongated below six times in a transverse direction has not only insufficient transverse tensile strength but also high tear strength. Such tape, therefore, has to be cut by cutting devices. Still worse, when a transverse force is applied to the tape, it will easily split in a longitudinal direction.

The film of high density polyethylene may have a thickness of 10 to 100μ, preferably 15 to 60μ. In case of the adhesive tape shown in FIG. 2, the film may most preferably have a thickness of 30 to 60μ, while in case of the paper adhesive tape shown in FIG. 3, the thickness of the film may be thinner, i.e. most preferably 15 to 30μ. In a thickness of less than 10μ, a predetermined strength cannot be obtained. On the contrary, above 100μ, the film loses its flexibility. Accordingly, the adhesive tape cannot adhere intimately onto concaved or convexed surfaces to be applied. Particularly, when the tape is applied to corners of a container, it will peel off due to high restorable properties.

In producing the film 20 of high density polyethylene, polyethylene of a density of not less than 0.94 g/cc is subjected to extrusion molding by means of an extruder equipped with a flat die and thereafter to elongation treatment at least six times in a transverse direction by means of an elongating machine of tenter type. An exposure surface 22 of the film may be treated with a finishing agent. Any known agents including urethane type, polyester type, silicone type, shellac, paraffin wax and fluorine type may be used. Of these agents, a 2% toluene solution of bridging type silicone may preferably be used. After treatment the film is dried.

In producing the adhesive tape 10 in FIGS. 1 and 2, the pressure sensitive adhesive 21 is applied to an inner surface 23 of the film 20. In contrast, where the paper adhesive tape 30 in FIG. 3 is made, the adhesive 21 is applied to the base paper material 31. As the paper material, kraft paper such as clupak kraft paper may preferably be used although any other paper known in the art can be utilized. The thickness of the paper may be between 30 and 150 g/m², preferably 40 and 100 g/m².

The pressure sensitive adhesive 21 which may be used according to the invention includes a solvent type such as rubber system or acryl system, an emulsion type such as acryl system or vinylacetate system and a hot-melting type such as EVA systems (ethylenevinyl acetate system), rubber system or rubber polyamide resin system. The adhesive may be directly applied to the film 20 or the base paper material 31 whether the solvent type or emulsion type adhesive may be used if applied at a temperature below 120° C. In case of adhesives which cannot be adhered above 120° C., the transferring method can preferably be used whether the adhesive is of the solvent type, the emulsion type or of the hot-melting type above referred to. Where the adhesive tape 10 is made, the transferring method may most preferably be used with the hot-melting type adhesives. Of the hot-melting type adhesives, the rubber system consisting of the following commercially available products may be most preferred;

    ______________________________________                                         Cariflex TR110 7 (Shell Chemical)                                              Polybutene LV-100                                                                               (Nisseki Resin Chemical)                                      Arkon M 100      (Arakawa Rinsan Chemical)                                     Shellflex 371    (Shell Chemical)                                              Anti-Oxidant BZ  (Ouchishinkoh Chemical)                                       ______________________________________                                    

Meanwhile, where the paper adhesive tape 30 is made, the acryl system of the emulsion type adhesive such as sold under the trade name "Nikasol TS TB 3" by Nippon Carbide Kogyo K.K. including polyacrylate system may be most preferably used by means of the transferring method. The film 20 can be conveniently adhered to the base paper material 31 by sandwiching an adhesive layer 32 of low density polyethylene between the film 20 and the paper material 31 by means of lamination rollers. Of course, any known method may be applied for the adhesion of the film 20 to the base paper material 31.

Although particular forms of the tapes 10 and 30 have been described herein, the pressure sensitive adhesive 21 may be applied on both sides of the film 20. In any case the thickness of the pressure sensitive adhesive layer may preferably be between 5μ and 200μ.

The adhesive tape according to the invention may be used for teaching materials such as coloured paper if the base paper material 31 is coloured while the film 20 is transparent or translucent or if the base paper material 31 is white while the film 20 is coloured. In any form, pigments are not exposed on the surface so that the adhesive tape or modified coloured paper is suitable for children's use from sanitary standpoint of view. The adhesive tape can also be utilized for labels if the base paper material 31 is printed to form patterns, figures, letters or a combination thereof on its surface.

THE EXAMPLES OF THE INVENTION EXAMPLE 1

High density polyethylene (density of 0.94 g/cc) M l 0.9) was subjected to molding by means of an extruder equipped with a flat die and thereafter to elongation at various magnifications in a transverse direction at 130° C. by means of an elongating machine of tenter type to form a film having a thickness of 60μ. To this film a 2% toluene solution of bridging type silicone was applied and dried at 80° C. for bridging. Then a layer of pressure sensitive adhesive having the following compositions (thickness of 30μ) was provided on the other side of the film by the transferring method.

    ______________________________________                                         Cariflex TR 110 7 (Shell Chemical)                                                                        100 parts                                           (Thermoplastic block copolymer of styrene system)                                                         by wt.                                              Arkon M-100 (Arakawa Rinsan Chemical)                                                                     175 parts                                           (Tackifier of modified wood rosin system)                                                                 by wt.                                              Shellflex 371 (Shell Chemical)                                                                            20 parts                                            (Naphthene system oil)     by wt.                                              Polybutene LV-100 (Nisseki Resin Chemical)                                                                5 parts                                             (Polybutene)               by wt.                                              Anti-Oxidant) BZ (Ouchishinroh Chemical)                                                                  5 parts                                             (Anti-Oxidant)             by wt.                                              ______________________________________                                    

The adhesive tape thus obtained was wound up to form a roll and cut into a plurality of rolls.

Various experiments were made. The result is given in Table I.

                                      Table 1                                      __________________________________________________________________________                        Transverse                       Whether or not                                tensile              Transverse  the tapes applied                     Magnification                                                                          strength                                                                              Sealing strength of                                                                          tear  Easiness                                                                             on the corners             Run Material                                                                              of transverse                                                                          (Kg/10mm                                                                              corrugated cardboard                                                                         strength                                                                             cut by                                                                               of the container           No. of film                                                                               elongation                                                                             in width)                                                                             container     (g)   hand  tucked                     __________________________________________________________________________                                                         up                              High density         The container broken at                              1   polyethylene                                                                          6       15.0   the 18th drop but                                                                            138   Easy  None                                                 the tape not torn                                                              At the 22nd drop the                                 2   "      8       16.4   container broken but                                                                         131   "     "                                                    the tape not torn                                                              At the 17th drop the                                 3   "      10      18.0   container broken but                                                                         120   "     "                                                    the tape not torn                                                              At the 18th drop the                                 4   "      12      19.1   container broken but                                                                         115   "     "                                                    the tape not torn                                                              At the 20th drop the                                 5   "      14      19.5   container broken but                                                                         109   "     "                                                    the tape not torn                                                              At the 21st drop the                                 6   "      16      21.2   container broken but                                                                         104   "     "                                                    the tape not torn                                                              At the 5th drop the                                  7   "      3       5.6    tape splitted 257   Difficult                                                                            "                                                    longitudinally                                                                 At the 11th drop the                                 8   "      5       7.3    tape splitted 205   Rather                                                                               "                                                    longitudinally      difficult                                                  At the 12th drop the                                 9   Polypro-                                                                              6       8.0    tape splitted 248   Difficult                                                                            The tape                       pylene                longitudinally            tucked up                                            At the 9th drop the                                  10  Polyvinyl-                                                                            6       5.3    tape splitted 293   "     "                              chloride              longitudinally                                       __________________________________________________________________________

In the experiments in Table I, the transverse tensile strength was determined in accordance with Japanese Industrial Standard Z-1539 (Hereinafter referred to JIS). The sample tape had a width of 150 mm.

The sealing strength of corrugated cardboard container was determined according to JIS-Z02020. A corrugated cardboard container (length 400 mm, width 330 mm, height 200 mm, thickness 5 mm), was packed with 200 rolls of vinyl adhesive tapes, each roll having a width of 19 mm and a length of 20 m (total weight of 18.4 kg.). The upper side and the bottom side of the container were sealed with the various tapes (width 50 mm) shown in Table I in the form of H figure. Then the container was dropped from an elevation of 1500 mm. The conditions of the container and the tapes were inspected.

The transverse tear strength was determined according to JIS-Z1523.

The easiness cut by hand was determined as follows: "Easy" means that the tapes were easily torn by one's hand right exactly in a transverse direction without using cutters.

"Difficult" means that even if cut by one's hand the tapes were not torn exactly in a transverse direction.

Whether or not the tape applied on the corners of the container tucked up was inspected in the following manners: The aforementioned container and the sample tapes were cooled in a room maintained at 0° C., where the container was sealed with the tapes in H figure and left for 3 days. The applied corners numbered as 1-5, 1-6, 3-5, 3-6, 5-1, 5-3, 6-1 and 6-3 in accordance with JIS-Z0201 were then inspected.

The Runs Nos. 7 through 10 are comparative examples. In Runs Nos. 7 and 8, the adhesive tapes were produced in the same manners as the preceding runs. However, the magnifications of the transverse elongation were 3 and 5, respectively.

In Run No. 9, polypropylene commercially available under trade name "Mitsubishi Noblen" was subjected to molding in the same manner as the preceding runs and thereafter to elongation transversely six times at 150° C. by means of a tenter to obtain a film of 60μ in thickness. The same pressure sensitive adhesive (thickness 30μ) was adhered to one side of the film and would up to obtain a roll.

In Run No. 10, 100 parts by weight of polyvinyl chloride commercially available under trade name "Denka Vinyl SS 110", 3 parts by weight of cadmium stearate and 1 part by weight of a stabilizer were mixted and molded by the casting method. Then the moldings were elongated six times at 85° C. in a transverse direction to obtain a film of 60μ in thickness. The adhesive tape was made of this film in the same manner as Run No. 9.

As is apparent from Table I, the adhesive tapes according to the invention have the transverse tensile strengths three times as strong as those according to the comparative examples. Nevertheless the tear strengths are half as compared with those according to the comparative examples. Furthermore, the sealing strengths are excellent and the tapes are easily cut by user's hand.

EXAMPLE 2

Adhesive tapes were made of high density polyethylene (density 0.95 g/cc M I 0.9) in the same manner as in Example 1. The tapes were transversely elongated at various magnifications.

The adhesive tapes thus obtained were placed in a room maintained at -40° C. and subjected to experiments similar to those according to Example I. The result is given in Table II.

                                      Table II                                     __________________________________________________________________________                Transverse                    Whether or not                                   tensile           Transverse  the tapes applied                        Magnification                                                                          strength                                                                             Sealing strength of                                                                        tear  Easiness                                                                             on the corners                        Run                                                                               of transverse                                                                          (kg/10 mm                                                                            corrugated cardboard                                                                       strength                                                                             cut by                                                                               of the container                      No.                                                                               elongation                                                                             in width)                                                                            container   (g)   hand  tucked up                             __________________________________________________________________________                      At the 12th drop                                              11 4       10.4  the tape splitted                                                                          201   Rather                                                                               None                                                   longitudinally    difficult                                                    At the 22nd drop                                              12 6       29.0  the container broken                                                                       118   Easy  "                                                      but the tape not torn                                                          At the 18th drop                                              13 8       31.6  the container broken                                                                       111   "     "                                                      but the tape not torn                                                          At the 17th drop                                              14 10      32.0  the container broken                                                                       106   "     "                                                      but the tape not torn                                                          At the 18th drop                                              15 12      36.4  the container broken                                                                       102   "     "                                                      but the tape not torn                                                          At the 16th drop                                              16 14      37.0  the container broken                                                                        99   "     "                                                      but the tape not torn                                                          At the 22nd drop                                              17 16      38.0  the container broken                                                                        98   "     "                                                      but the tape not torn                                         __________________________________________________________________________      Note:                                                                          Run No. 11 is a comparative example.                                     

As is apparent from Table II, the adhesive tapes according to the invention have enhanced transverse tensile strengths even under -40° C. as well as lowered tear strengths. As far as sealing strength and tucking-up are concerned, no inferior properties are observed. Hence, the adhesive tape can be efficiently used at low temperatures.

EXAMPLE 3

High density polyethylene having a density of 0.96 g/cc was extruded through a flat die and then elongated transversely ten times by means of an elongating machine of the tenter type to obtain a film having a thickness of 20μ.

The film thus obtained was adhered to a base paper material with a layer of low density polyethylene having a thickness of 15μ being sandwiched between the base paper material and the film and laminated by rollers. As the base paper material, clupak kraft paper having a weight per m² of 73 g/m² was used.

Then on the other side of the paper material a pressure sensitive adhesive was applied by means of a coating machine to have a thickness of 40μ and dried at 110° to 130° C. The tapes thus obtained was wound up to form a roll and cut to have a width of 50 mm. The pressure sensitive adhesive has the following compositions:

    ______________________________________                                         Natural rubber - MMA-AN graftpolymer                                                                      4.1 parts                                                                      by wt.                                              Terpene resin              1.8 parts                                                                      by wt.                                              Zinc white                 0.15 parts                                                                     by wt.                                              Trimethylthiuram disulfide 0.06 parts                                                                     by wt.                                              Toluene                    6.0 parts                                                                      by wt.                                              ______________________________________                                    

The paper adhesive tapes thus obtained were subjected to various experiments. The result is given in Table III.

                                      Table III                                    __________________________________________________________________________             The paper adhesive                                                                      Known   Known reinforced                                                                        Known                                                tape according                                                                          kraft adhesive                                                                         paper adhesive                                                                          fabric adhesive                              Test    to the invention                                                                        tape    tape     tape                                         __________________________________________________________________________     Temperature                                                                            20  -20  20      20       20                                           (° C.)                                                                  Transverse                                                                     tensile                                                                        strength                                                                               12.4                                                                               12.5 4.7     6.8      7.8                                          (kg/10mm                                                                       in width)                                                                      Transverse                                                                             18.3                                                                               16.3 5.0     10.9     6.8                                          elongation                                                                     (%)                                                                            Transverse                                                                     tear strength                                                                          290 293  280     550      720                                          (g)                                                                            The conditions                                                                 of cut edges                                                                           Good                                                                               Good Poor    Poor     Good                                         __________________________________________________________________________

In the experiments in Table III, the transverse tensile strength and the transverse elongation were determined according to JIS Z-1523. The transverse tear strength was determined according to JIS L-1004. The conditions of cut edges were determined by observing the edges of the tapes torn at a rate of 30 m/mm, each tape having had a notch of 3 mm in a transverse direction from the edge. "Good" means that the tape was torn exactly transversely, whereas "Poor" means that the tape was almost not torn transversely.

For the purpose of comparison, a kraft adhesive tape, a reinforced paper adhesive tape and a fabric adhesive tape commercially available under trade names "Nittoh Kraft Tape 7100", "Krapack 7150" and "Nittoh Nuno Tape" (Each produced by Nittoh Denki Kogyo K.K.), respectively were used.

From Table III it can be seen that the paper adhesive tape of the invention has transverse tensile strength several times as strong as the known kraft adhesive tape. Furthermore, the paper adhesive tape of the invention has larger transverse tensile strength than the known reinforced paper adhesive tape which are used for sealing containers containing heavy contents. The transverse tear strength of the paper adhesive tape according to the invention can be torn exactly in a transverse direction with a force almost equal to that required for the kraft adhesive tape of the known type. In addition, the strengths at room temperature are almost the same as those at -20° C.

EXAMPLE 4

The paper adhesive tapes were made in the same manner as in Example 3 except that the high density polyethylene films were elongated at various magnifications.

The result is given in Table IV.

                  Table IV                                                         ______________________________________                                                                  Transverse                                                                               The                                         Magnification                                                                            Transverse     tear      conditions                                  of transverse                                                                            tensile strength                                                                              strength  of                                          elongation                                                                               (kg/10mm in width)                                                                            (g)       cut edges                                   ______________________________________                                         0         5.2            530       Poor                                        4         6.5            380       *                                           6         9.5            310       Good                                        8         11.3           285       "                                           10        12.4           292       "                                           12        12.6           275       "                                           14        13.5           280       "                                           ______________________________________                                          Note:                                                                          * 10% of the test samples were not torn in a transverse direction.       

The conditions of the cut edges were determined in accordance with Example 3.

As shown in Table IV, with a magnification of transverse elongation of not less than six, satisfactory results are obtained.

Further experiments were effected using the same paper adhesive tapes. However, the thickness of the high density polyethylene film was varied. The result is shown in Table V.

                  Table V                                                          ______________________________________                                         Transverse tensile strength (kg/10mm in width)                                         Magnification of                                                       Thickness                                                                              tensile                                                                (mm)    elongation   6       8     10    12                                    ______________________________________                                         0.008            5.0     5.6     5.8   --                                      0.010            6.5     7.3     7.6   7.8                                     0.020            9.5     11.3    12.4  12.6                                    0.030            9.3     12.1    12.8  13.9                                    0.040            10.1    13.6    14.5  15.8                                    0.060            10.7    14.7    15.7  17.2                                    ______________________________________                                          Note:                                                                          The tensile strength was determined according to JIS Z1523.              

With the adhesive tape comprising a film of a thickness of less than 0.010 mm, a satisfactory transverse tensile strength was not obtained. On the other hand, with the adhesive tape having a film of a thickness of more than 0.050 mm, favourable flexibility was not attained.

Although the present invention has been described with reference to preferred embodiments and examples, various modifications and variations can be made without departing from the spirit of the invention. It is intended that all these modifications and variations be included. 

What is claimed is:
 1. An adhesive tape comprising a film of high density polyethylene having a density of not less than 0.94 g/cc elongated six to sixteen times only transversely to the longitudinal direction of the tape and a layer of pressure sensitive adhesive applied at least on one side of said elongated film of high density polyethylene, said film of high density polyethylene having a thickness of 30 to 60μ.
 2. The adhesive tape as claimed in claim 1 wherein said film of high density polyethylene is elongated at least ten times only transversely to the longitudinal direction of the tape.
 3. The adhesive tape as claimed in claim 1 wherein said layer of pressure sensitive adhesive is applied to said one side of the film of high density polyethylene.
 4. The adhesive tape as claimed in claim 1 wherein a second layer of pressure sensitive adhesive is applied to the other side of said film of high density polyethylene.
 5. The adhesive tape as claimed in claim 1 wherein said adhesive tape is in the form of a roll. 